ACSS试制数据外层重拉退火后4.docx

《ACSS试制数据外层重拉退火后4.docx》由会员分享，可在线阅读，更多相关《ACSS试制数据外层重拉退火后4.docx（2页珍藏版）》请在第一文库网上搜索。

1、2010年7月份广东远光电缆实业有限公司ACSS/TW-400/50产品试制数据（退火后）序号实测电阻室内温度eC重量g长度m横截面积mm2拉断力N强度MPa伸长率%退火后电阻率.nm7m退火后相对IAeS值10.2794X1O224.36.7920.2549.892893795260.02717363.4%20.280510224.06.5920.2489.8338922940.02714963.5%30.2790X1O224.36.8570.2579.870989290280.02707463.7%40.2802X1O224.26.4200.2419.855389291240.027158

2、63.5%50.2800IO224.07.2160.2729.814887689250.02704963.7%60.2789IO223.96.9430.2609.879386688280.02713063.5%70.280410223.87.2530.2729.865190492260.02724863.3%80.2831IO223.96.9590.2649.752188190220.02718463.4%90.279310224.16.7140.2519.896090191230.02719463.4%100.279410224.36.6330.2489.894986587270.02717

3、963.4%110.2798X1023.76.4730.2439.854990292240.02717263.5%120.2796IO223.87.3900.2779.870087989250.02718363.4%130.2801IO223.87.5870.2859.848790292一0.02717363.4%140.279310223.87.8440.2949.870688389240.02715663.5%150.279710223.87.3000.2749.856691092240.02715663.5%160.2810X1023.76.8050.2569.834389191250.

4、02723163.3%170.281210223.76.5890.2499.789886288260.02712763.6%180.2787X1O223.87.3170.2749.879585787230.02712263.6%注：以上数据为外层线及拉制外层线所用铝杆数据（拉丝油的原因导致退火后表面质量不合格重新拉制）。退火温度为350,保温时间为15Omin1）2010年7月份广东远光电缆实业有限公司ACSS/TW-400/50产品试制数据（退火后）序号实测电阻室内温度9C重量S长度m横截面积mm拉断力N强度MPa伸长率%退火后电阻率C.mm7m退火后相对IAcS值190.279410223.87.0670.2659.866089891260.02715363.5%200.2798X1O223.86.4120.2419.843189491250.02712963.6%21222324252627282930313233343536注：以上数据为外层线及拉制外层线所用铝杆数据（拉丝油的原因导致退火后表面质量不合格重新拉制）。退火温度为350,保温时间为15Omin。